Basic Properties, Synthesis and Typical Properties of Boron Carbide

What is boron caride? Boron Carbide powder is part of the trigonal crystal structure. Unit cell contains 12 B and 3 C elements. C atoms within a unit cell are connected in a stereo diagonal arrangement. This configuration can be changed by B atoms. B4C’s molecular mass is 52.25. C21.74% and B78.25%. B4C can be found in a range of colors, including gray to black. The powder also has a high grind efficiency, with 60-70% of SiC and 1-2 times the grinding efficiency for corundum. B4C powder melts at 2450°C (decomposition). The coefficient of expansion for 1000°C at 4.510-6°C-1 is At 100°C, the thermal conductivity of B4C powder at 1000°C was 121.4W/mk. It is 62.3W/mk for 700°C. Hot-pressed B4C product can also be used as heat-resistant and wear-resistant components. B4C can be used in the refractory industries as an additive. For example, it is added to carbon-bonded materials to act an antioxidant. A body with unshaped materials has a higher strength and greater resistance to corrosion.

Synthesis of Boron carbide

and its typical properties

To synthesize B4C powder, the common technique is to combine boron anhydride and excess carbon.

2B2O3+7C→B4+6CO↑

You can either use an electric arc furnace or a muffle oven to perform the reaction. The resistance furnace can synthesize B4C by heating the mixture B2O3-carbon C at a temperature below B4C. (sometimes with Free B 1%-2%) is another better method. B4C is decomposed at 2200 when it is made in an electric furnace. This is because of the high arc temperatures. The quality of B4C produced is affected by the volatilization of some of its components, which can result in a high level of C (usually between 20-30%) in the reaction products. Boric acid, artificial graphite, fixed carbon greater that 95%), and petroleum coke (fixed carb greater than 15%) are all used in the production of B4C. About 2% is the theoretical amount. 50 percent of the total carbon addition amount comes from petroleum coke and artificial graphite. This is about 3%-4% higher than the theoretical value. By reducing or carbonizing the furnace between 1700 and 2300, the three ingredients can be mixed together in a mill. To obtain different particle sizes of B4C, the frit must be separated, washed, pickedled, crushed, ground and pickled. Buffalotours (aka. Buffalotours advanced materials. We are a global supplier of chemical materials and manufacturer. Our company has over 12 years’ experience in manufacturing super-high-quality chemicals. We produce B4C powder with high purity and fine particles. We can help you if the price is lower.
Inquiry us