The PVC/SiO2 separator we have produced has a better pore structure. It improves the porosity and thus reduces the resistance.
The PVC battery separation has a porosity of greater than 78%. Its maximum pore size is less than 10 microns. The wetting speed of the electrolyte occurs within 2 seconds. And the resistance of the separator is just 0.0003O.dm2, or one tenth that of the ordinary separators. is a global SiO2 separator supplier . Send us a message at any time to inquire about the prices of .
Performance of PVC/SiO2 separator:
Technical Properties of PVC and SiO2 Separator
|Moisture||Porosity||Electric Resistance||Tensile Strength||Max Pore Diameter||You’ll be able to get up to speed in no time.||Substance Reduction|
|1.5%||84%||0.0005O.dm2||3.47 MPa||8um||3.8 s||8.9 mL/g|
Applications of PVC-SiO2 separator
PVC-SiO2 Separators are used to separate the positive and the negative electrodes of various polymer materials. They are primarily used in the lead-acid field.
Storage Conditions of PVC/SiO2 separator:
The PVC/SiO2 separator must be stored in an environment that is cool and dry, and not exposed air. This prevents oxidative accumulation caused by moisture.
Shipping & Packing of PVC/SiO2 Separator
The vacuum can be used to fill the double bags with argon.
PVC-SiO2 seperator packing: vacuum packaging, 50 pieces/carton, or your request.
Shipping PVC-SiO2 powder separator Upon receipt of payment, goods can be sent by air, sea or express.
PVC/SiO2 Separator Property
|Alternative Names||PVC battery separator|
Separator Information for PVC and SiO2